ITEM | UNIT | TESTING METHOD | 300AR | 400AR | 500AR | ||
PHYSICAL PROPERTIES | SPECIFIC GRAVITY | g/cm3 | ISO 1183 | 1.16 | 1.16 | 1.14 | |
TOTAL LIGHT TRANSMITANCE | % | ISO 13468 | 92 | 92 | 91 | ||
HAZE | % | ISO 14782 | 0.5 | 0.6 | 0.6 | ||
REFRACTIVE INDEX | - | nd | 1.49 | 1.49 | 1.49 | ||
WATER ABSORPTION | % | 24HR | 0.3 | 0.3 | 0.3 | ||
THERMAL PROPERTIES | SPECIFIC HEAT | J/(g‧K) | JIS K7123 | 1.5 | 1.5 | 1.5 | |
HEAT DISTORTION TEMPERATURE | ℃ | ISO 75 | 85 | 92 | 86 | ||
VICAL SOFTING TEMPERATURE | ℃ | ISO 306 | 85 | 93 | 83 | ||
MELT FLOW RATE | g/10min | ISO 1133 | 6 | 1.1 | 1.3 | ||
MECHANICAL PROPERTIES | TENSILE STRENGTH | MPa | ISO 527 | 58 | 52 | 40 | |
ELONGATION | % | ISO 527 | 43 | 45 | 55 | ||
MODULUS OF ELASTICITY | GPa | ISO 527 | 1.8 | 1.9 | 1.4 | ||
FLEXURAL STREMGTH | MPa | ISO 178 | 76 | 76 | 62 | ||
FLEXURAL MODULUS | GPa | ISO 178 | 1.9 | 1.9 | 1.5 | ||
IZOD IMPACT STRENGTH IZOD | kJ/m2 | ISO 180 | 3.7 | 5.5 | 7.5 | ||
ROCKWELL HARDNESS | - | ISO 2039 | 113 | 110 | 90 | ||
ELECTRIC PROPERTIES | SURFACE RESISTIVITY | Ω | JIS K6911 | >1016 | >1016 | >1016 | |
DIELETRIC CONSTANT | 60Hz | JIS K6911 | 3.7 | 3.7 | 3.7 | ||
POWER FACTOR | 60Hz | JIS K6911 | 0.05 | 0.05 | 0.05 | ||
MOULD SHRINKAGE | % | 0.4-0.8 | 0.4-0.8 | 0.4-0.8 | |||
REMARKS | THEDATA ARE INTENDED AS A GENERAL GUIDE ONLY AND NECESSARILY REPRESENT RESULTS THAT MAY BE OBTAINED ELSEWHERE. |